- 密度 [g/cm3]: 0.0521
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0521 g/cc | 0.00188 lb/in3 | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 1.10 MPa | 160 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 3.5 % | 3.5 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.0500 GPa | 7.25 ksi | ISO 527-2, ASTM D 638 |
| Compressive Strength | 0.700 MPa | 102 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Poissons Ratio | 0.25 | 0.25 | Calculated |
| Shear Modulus | 0.0200 GPa | 2.90 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 0.600 MPa | 87.0 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Heat Distortion Resistance; DIN 53424 |