- 密度 [g/cm3]: 0.191
- 斷裂伸長率 [%]: 11.8
- 彎曲強(qiáng)度 [MPa]: 8.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.191 g/cc | 0.00689 lb/in3 | ASTM D1622-63 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 8.34 MPa | 1210 psi | ASTM D638-68 | ||
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638-68 | ||
| Modulus of Elasticity | 0.372 GPa | 54.0 ksi | ASTM D638-68 | ||
| Flexural Yield Strength | 11.8 MPa | 1710 psi | Perpendicular to Sheet; ASTM D 790-66 | ||
| 12.3 MPa | 1780 psi | ASTM D790-66 | |||
| Compressive Yield Strength | 3.14 MPa | 455 psi | Perpendicular to Sheet; ASTM D 1621-64 | ||
| 7.65 MPa | 1110 psi | ASTM D1621-64 | |||
| Shear Modulus | 0.0979 GPa | 14.2 ksi | ASTM C273-61 | ||
| Shear Strength | 2.94 MPa | 427 psi | Perpendicular to Sheet; ASTM C 273-61 | ||
| 5.39 MPa | 782 psi | ASTM C273-61 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | Dimensional stability per DIN 53424; oriented cell structure starts to decrease beyond this temperature. | ||
| Descriptive Properties | |||||
| Color | White | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.