- 密度 [g/cm3]: 0.11
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.110 g/cc | 0.00398 lb/in3 | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 3.50 MPa | 508 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 4.5 % | 4.5 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.160 GPa | 23.2 ksi | ISO 527-2, ASTM D 638 |
| Flexural Strength | 4.50 MPa | 653 psi | DIN 53423, ISO 1209, ASTM D 790 |
| Compressive Strength | 3.00 MPa | 435 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Shear Modulus | 0.0500 GPa | 7.25 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 2.40 MPa | 348 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Heat Distortion Resistance; DIN 53424 |