- 拉伸強度 [MPa]: 18.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | |
| Tensile Strength, Yield | 18.1 MPa | 2620 psi | |
| Elongation at Yield | 283 % | 283 % | |
| 100% Modulus | 0.0105 GPa | 1.52 ksi | |
| 200% Modulus | 0.01616 GPa | 2.344 ksi | |
| Tear Strength | 71.4 kN/m | 407 pli | Die C |
| Compression Set | 78 % @Temperature 70.0 °C, Time 79200 sec | 78 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 30.0 min @Temperature 154 °C | 0.500 hour @Temperature 310 °F | Press cured |