- 拉伸強度 [MPa]: 19.28
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 61 | 61 | |
| Tensile Strength, Yield | 19.28 MPa | 2796 psi | |
| Elongation at Yield | 418 % | 418 % | |
| 100% Modulus | 0.00472 GPa | 0.685 ksi | |
| 200% Modulus | 0.009811 GPa | 1.423 ksi | |
| 300% Modulus | 0.01333 GPa | 1.934 ksi | |
| Tear Strength | 43.4 kN/m | 248 pli | Die C |
| Compression Set | 55 % @Temperature 70.0 °C, Time 79200 sec | 55 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 38.0 min @Temperature 154 °C | 0.633 hour @Temperature 310 °F | Press cured |