- 拉伸強(qiáng)度 [MPa]: 25.19
- 脆化溫度 [℃]: -35.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |||
| 82 | 82 | heat aged 70 hours @ 100oC | |||
| Tensile Strength, Yield | 25.19 MPa | 3653 psi | |||
| Elongation at Yield | 490 % | 490 % | |||
| 100% Modulus | 0.00552 GPa | 0.801 ksi | |||
| 200% Modulus | 0.01275 GPa | 1.849 ksi | |||
| 300% Modulus | 0.01904 GPa | 2.761 ksi | |||
| Tear Strength | 63.0 kN/m | 359 pli | Die C | ||
| Compression Set | 32.3 % @Temperature 70.0 °C, Time 79200 sec | 32.3 % @Temperature 158 °F, Time 22.0 hour | |||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -35.0 °C | -31.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 8.00 min @Temperature 155 °C | 0.133 hour @Temperature 311 °F | |||
| Descriptive Properties | |||||
| Weight Loss (%) | 1.5 | heat aged 70 hours @ 100oC | |||