- 拉伸強度 [MPa]: 28.55
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 28.55 MPa | 4141 psi | |
| Elongation at Yield | 475 % | 475 % | |
| 100% Modulus | 0.00192 GPa | 0.278 ksi | |
| 200% Modulus | 0.00527 GPa | 0.764 ksi | |
| 300% Modulus | 0.01211 GPa | 1.757 ksi | |
| Tear Strength | 58.7 kN/m | 335 pli | Die C |
| Compression Set | 29 % @Temperature 100 °C, Time 79200 sec | 29 % @Temperature 212 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 160 °C | 0.250 hour @Temperature 320 °F | |