- 拉伸強度 [MPa]: 30.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 63 | 63 | |
| Tensile Strength, Yield | 30.1 MPa | 4370 psi | |
| Elongation at Yield | 615 % | 615 % | |
| 100% Modulus | 0.00290 GPa | 0.420 ksi | |
| 200% Modulus | 0.00641 GPa | 0.930 ksi | |
| 300% Modulus | 0.01134 GPa | 1.645 ksi | |
| Tear Strength | 60.4 kN/m | 345 pli | Die C |
| Compression Set | 36 % @Temperature 70.0 °C, Time 79200 sec | 36 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 6.40 min @Temperature 155 °C | 0.107 hour @Temperature 311 °F | ts2 |
| 12.0 min @Temperature 155 °C | 0.200 hour @Temperature 311 °F | TC90 | |