- 拉伸強度 [MPa]: 27.56
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | |
| Tensile Strength, Yield | 27.56 MPa | 3997 psi | |
| Elongation at Yield | 628 % | 628 % | |
| 100% Modulus | 0.00245 GPa | 0.356 ksi | |
| 200% Modulus | 0.00534 GPa | 0.774 ksi | |
| 300% Modulus | 0.009487 GPa | 1.376 ksi | |
| Tear Strength | 65.0 kN/m | 371 pli | Die C |
| Compression Set | 49.4 % @Temperature 70.0 °C, Time 79200 sec | 49.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 34.2 min @Temperature 155 °C | 0.570 hour @Temperature 311 °F | TC90 |