- 拉伸強度 [MPa]: 22.14
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 22.14 MPa | 3211 psi | |
| Elongation at Yield | 659 % | 659 % | |
| 100% Modulus | 0.00125 GPa | 0.181 ksi | |
| 200% Modulus | 0.00224 GPa | 0.325 ksi | |
| 300% Modulus | 0.00460 GPa | 0.667 ksi | |
| Tear Strength | 40.8 kN/m | 233 pli | Die C |
| Compression Set | 44 % @Temperature 100 °C, Time 79200 sec | 44 % @Temperature 212 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 160 °C | 0.250 hour @Temperature 320 °F | |