- 拉伸強度 [MPa]: 32.23
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 32.23 MPa | 4675 psi | |
| Elongation at Yield | 555 % | 555 % | |
| 100% Modulus | 0.00362 GPa | 0.525 ksi | |
| 200% Modulus | 0.008294 GPa | 1.203 ksi | |
| 300% Modulus | 0.01444 GPa | 2.094 ksi | |
| Tear Strength | 65.5 kN/m | 374 pli | Die C |
| Compression Set | 29.6 % @Temperature 70.0 °C, Time 79200 sec | 29.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.4 min @Temperature 155 °C | 0.173 hour @Temperature 311 °F | TC90 |