- 彎曲強度 [MPa]: 10.5
- 脆化溫度 [℃]: -45.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 73 @Temperature 100 °C | 73 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 73 | 73 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 10.5 MPa | 1520 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 344 % | 344 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00240 GPa | 0.348 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00440 GPa | 0.638 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00760 GPa | 1.10 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00930 GPa | 1.35 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 31.6 kN/m | 180 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 82 % @Temperature 125 °C | 82 % @Temperature 257 °F | Pellets cured MDR t'95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -45.0 °C | -49.0 °F | Temperature Retraction, TR-10 |