- 密度 [g/cm3]: 1.339
- 彎曲強度 [MPa]: 7.0
- 脆化溫度 [℃]: -15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.339 g/cc | 0.04837 lb/in3 | |
| Mooney Viscosity | 21 @Temperature 100 °C | 21 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 61 | 61 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 7.00 MPa | 1020 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 492 % | 492 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00200 GPa | 0.290 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00390 GPa | 0.566 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 300% Modulus | 0.00520 GPa | 0.754 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 31.0 kN/m | 177 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 75 % @Temperature 125 °C | 75 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -15.0 °C | 5.00 °F | Temperature Retraction, TR-10 |