- 彎曲強度 [MPa]: 14.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 55 @Temperature 100 °C | 55 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 69 | 69 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 14.4 MPa | 2090 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Modulus of Elasticity | 0.00130 GPa | 0.189 ksi | 25% Modulus, Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00200 GPa | 0.290 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.00380 GPa | 0.551 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 200% Modulus | 0.00800 GPa | 1.16 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 26.3 kN/m | 150 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 35 % @Temperature 100 °C | 35 % @Temperature 212 °F | 22 hr |