- 密度 [g/cm3]: 1.064
- 彎曲強(qiáng)度 [MPa]: 26.1
- 脆化溫度 [℃]: -28.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.064 g/cc | 0.03844 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 74 | 74 | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Tensile Strength, Ultimate | 26.1 MPa | 3790 psi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Elongation at Break | 266 % | 266 % | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 100% Modulus | 0.00560 GPa | 0.812 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| 200% Modulus | 0.0170 GPa | 2.47 ksi | Vulcanizate, Press cured, TC95 +3min at 180°C |
| Tear Strength | 30.6 kN/m | 175 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 180°C |
| Compression Set | 61 % @Temperature 125 °C | 61 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min, 70 hr; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -28.0 °C | -18.4 °F | Temperature Retraction, TR-10 |