- 彎曲強度 [MPa]: 20.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 20.9 MPa | 3030 psi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 210 % | 210 % | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00990 GPa | 1.44 ksi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 27 % @Temperature 200 °C | 27 % @Temperature 392 °F | Method B, O-rings, 70 hr |