- 彎曲強度 [MPa]: 15.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 89 | 89 | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 15.9 MPa | 2310 psi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 165 % | 165 % | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.0126 GPa | 1.83 ksi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 33 % @Temperature 200 °C | 33 % @Temperature 392 °F | Method B, O-rings, 70 hr |