- 彎曲強度 [MPa]: 15.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 15.5 MPa | 2250 psi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 240 % | 240 % | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00720 GPa | 1.04 ksi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 29 % @Temperature 200 °C | 29 % @Temperature 392 °F | Method B, O-rings, 70 hr |