- 彎曲強度 [MPa]: 13.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 66 | 66 | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Tensile Strength, Ultimate | 13.9 MPa | 2020 psi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Elongation at Break | 280 % | 280 % | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| 100% Modulus | 0.00310 GPa | 0.450 ksi | Cured 10 min at 177°C and Post Cured 16 hr at 200°C |
| Compression Set | 27 % @Temperature 200 °C | 27 % @Temperature 392 °F | Method B, O-rings, 70 hr |