- 彎曲強(qiáng)度 [MPa]: 11.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 77 @Temperature 121 °C | 77 @Temperature 250 °F | ML 1 + 10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 79 | 79 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Tensile Strength, Ultimate | 11.9 MPa | 1730 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Elongation at Break | 230 % | 230 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 24 % @Temperature 200 °C | 24 % @Temperature 392 °F | Method B, Plied Disks, 70 hr |