- 彎曲強度 [MPa]: 11.4
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 11.4 MPa | 1650 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 150 % | 150 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00910 GPa | 1.32 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tear Strength | 19.3 kN/m | 110 pli | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 11 % @Temperature 200 °C | 11 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |