- 彎曲強(qiáng)度 [MPa]: 12.7
- 脆化溫度 [℃]: -19.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 12.7 MPa | 1840 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 205 % | 205 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00630 GPa | 0.914 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tear Strength | 25.6 kN/m | 146 pli | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 20 % @Temperature 200 °C | 20 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -19.0 °C | -2.20 °F | Temperature Retraction, TR-10; ASTM D1329 |
| Glass Transition Temp, Tg | -20.2 °C | -4.36 °F | DSC |