| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 14.3 MPa | 2070 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 175 % | 175 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00830 GPa | 1.20 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tear Strength | 22.1 kN/m | 126 pli | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 12 % @Temperature 200 °C | 12 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |