- 彎曲強度 [MPa]: 9.6
- 脆化溫度 [℃]: -19.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
| Tensile Strength, Ultimate | 9.60 MPa | 1390 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Elongation at Break | 365 % | 365 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| 100% Modulus | 0.00290 GPa | 0.421 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Tear Strength | 25.9 kN/m | 148 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 44 % @Temperature 200 °C | 44 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -19.0 °C | -2.20 °F | Temperature Retraction on Post Cured Specimens, TR-10; ASTM D1329-88 |
| Glass Transition Temp, Tg | -19.5 °C | -3.10 °F | DSC at 20°C/min on Post Cured Specimens |