- 彎曲強度 [MPa]: 15.7
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 15.7 MPa | 2280 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 250 % | 250 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00560 GPa | 0.812 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tear Strength | 25.7 kN/m | 147 pli | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 10 % @Temperature 200 °C | 10 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |