- 彎曲強度 [MPa]: 10.5
- 脆化溫度 [℃]: -16.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 10.5 MPa | 1520 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 215 % | 215 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00520 GPa | 0.754 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tear Strength | 24.7 kN/m | 141 pli | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 17 % @Temperature 200 °C | 17 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -16.0 °C | 3.20 °F | Temperature Retraction, TR-10; ASTM D1329 |
| Glass Transition Temp, Tg | -16.5 °C | 2.30 °F | DSC |