- 彎曲強度 [MPa]: 12.3
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tensile Strength, Ultimate | 12.3 MPa | 1780 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Elongation at Break | 160 % | 160 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| 100% Modulus | 0.00740 GPa | 1.07 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412 |
| Tear Strength | 22.8 kN/m | 130 pli | Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 17 % @Temperature 200 °C | 17 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414 |