- 密度 [g/cm3]: 1.69
- 吸水率 [%]: 0.05
- 彎曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.860 g/cc | 0.0311 lb/in3 | ISO 60 | ||
| Density | 1.69 g/cc | 0.0611 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.050 % | 0.050 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ISO 527-1 | ||
| Elongation at Break | 0.38 % | 0.38 % | ISO 527-1 | ||
| Tensile Modulus | 18.0 GPa | 2610 ksi | ISO 527-1 | ||
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 | ||
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 | ||
| Compressive Strength | 166 MPa | 24100 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.360 J/cm2 | 1.71 ft-lb/in2 | ISO 179-1 | ||
| Charpy Impact, Notched | 0.140 J/cm2 | 0.666 ft-lb/in2 | ISO 179-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 μm/m-°C | 7.78 μin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 32.0 μm/m-°C | 17.8 μin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 175 °C | >= 347 °F | ISO 75 Af | ||
| Shrinkage | 0.090 % | 0.090 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||