- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.55
- 缺口沖擊強度: 0.24
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 6.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | ASTM D1895 |
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| Water Absorption | 0.55 % | 0.55 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0085 cm/cm | 0.0085 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 0.79 % | 0.79 % | ASTM D638 |
| Tensile Modulus | 7.80 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | ASTM D790 |
| Flexural Modulus | 6.40 GPa | 928 ksi | ASTM D790 |
| Compressive Strength | 182 MPa | 26400 psi | ASTM D695 |
| Poissons Ratio | 0.30 | 0.30 | ASTM D638 |
| Shear Modulus | 3.00 GPa | 435 ksi | Calculated |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.227 J/cm2 | 1.08 ft-lb/in2 | ASTM D256 |
| Impact | 193 | 193 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.60e+11 ohm-cm | 6.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.1 | 5.1 | ASTM D150 |
| Dielectric Strength | 9.70 kV/mm | 246 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.055 | 0.055 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 51.0 μm/m-°C @Temperature 40.0 - 130 °C | 28.3 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.400 W/m-K @Temperature 100 °C | 2.78 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 183 °C | 361 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Oxygen Index | 27.1 % | 27.1 % | ASTM D2863 |
| Shrinkage | 0.39 % | 0.39 % | 72 hr, 120oC; ASTM D1299 |