- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.48
- 缺口沖擊強度: 0.264
- 彎曲強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 6.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.540 g/cc | 0.0195 lb/in3 | ASTM D1895 |
| Density | 1.42 g/cc | 0.0513 lb/in3 | ASTM D792 |
| Water Absorption | 0.48 % | 0.48 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0036 cm/cm | 0.0036 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 68 | 68 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 0.85 % | 0.85 % | ASTM D638 |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ASTM D638 |
| Flexural Strength | 77.0 MPa | 11200 psi | ASTM D790 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
| Compressive Strength | 158 MPa | 22900 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 2.74 GPa | 397 ksi | Calculated |
| Izod Impact, Notched | 0.264 J/cm | 0.495 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.300 J/cm2 | 1.43 ft-lb/in2 | ASTM D256 |
| Impact | 215 | 215 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.60e+12 ohm-cm | 2.60e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 6.8 | 6.8 | ASTM D150 |
| Dielectric Strength | 9.70 kV/mm | 246 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.069 | 0.069 | ASTM D150 |
| Arc Resistance | 140 sec | 140 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 μm/m-°C @Temperature 40.0 - 130 °C | 30.0 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.420 W/m-K @Temperature 100 °C | 2.91 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 188 °C | 370 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 5.10 mm | V-0 @Thickness 0.201 in | |
| Oxygen Index | 28.5 % | 28.5 % | ASTM D2863 |
| Shrinkage | 0.42 % | 0.42 % | 72 hr, 120oC; ASTM D1299 |
- 關(guān)鍵詞:
- 供應
- Compression Molded
- 酚醛樹脂
- Nodular
- Plenco 7080 Phenolic