- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.204
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 7.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.520 g/cc | 0.0188 lb/in3 | ASTM D1895 |
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0069 cm/cm | 0.0069 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 0.78 % | 0.78 % | ASTM D638 |
| Tensile Modulus | 7.70 GPa | 1120 ksi | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Compressive Strength | 218 MPa | 31600 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 2.83 GPa | 410 ksi | Calculated |
| Izod Impact, Notched | 0.204 J/cm | 0.382 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.206 J/cm2 | 0.980 ft-lb/in2 | ASTM D256 |
| Impact | 119 | 119 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.90e+11 ohm-cm | 3.90e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.8 | 4.8 | ASTM D150 |
| Dielectric Strength | 11.1 kV/mm | 282 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.051 | 0.051 | ASTM D150 |
| Arc Resistance | 128 sec | 128 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 58.0 μm/m-°C @Temperature 40.0 - 130 °C | 32.2 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.360 W/m-K @Temperature 100 °C | 2.50 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 24.7 % | 24.7 % | ASTM D2863 |
| Shrinkage | 0.253 % | 0.253 % | 72 hr, 120oC; ASTM D1299 |