- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.25
- 斷裂伸長率 [%]: 87.1
- 彎曲強度 [MPa]: 61.8
- 彎曲模量 [MPa]: 7.38
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.630 g/cc | 0.0228 lb/in3 | Apparent density per ASTM D1895 |
| Water Absorption | 0.25 % | 0.25 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | per ATM D955. Post shrinkage is 0.4% at 72hr 120oC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 61.8 MPa | 8960 psi | ASTM D638 |
| Elongation at Break | 1.32 % | 1.32 % | ASTM D638 |
| Tensile Modulus | 8.97 GPa | 1300 ksi | ASTM D638 |
| Flexural Yield Strength | 87.1 MPa | 12600 psi | ASTM D790 |
| Flexural Modulus | 7.38 GPa | 1070 ksi | ASTM D790 |
| Compressive Yield Strength | 210.6 MPa | 30550 psi | ASTM D695 |
| Charpy Impact, Notched | 0.210 J/cm2 | 0.999 ft-lb/in2 | ASTM D256 |
| Impact | 122 | 122 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.71e+11 ohm-cm | 1.71e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz | 5.0 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 12.6 kV/mm | 320 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.045 @Frequency 1e+6 Hz | 0.045 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 100 sec | 100 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 198 °C | 388 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |