- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.247
- 缺口沖擊強度: 0.18
- 彎曲強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in3 | ASTM D1895 |
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Water Absorption | 0.247 % | 0.247 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0061 cm/cm | 0.0061 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 89 | 89 | ASTM D785 |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D638 |
| Elongation at Break | 0.41 % | 0.41 % | ASTM D638 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Compressive Strength | 215 MPa | 31200 psi | ASTM D695 |
| Izod Impact, Notched | 0.180 J/cm | 0.337 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.194 J/cm2 | 0.923 ft-lb/in2 | ASTM D256 |
| Impact | 96 | 96 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 186 °C | 367 °F | ASTM D648 |
| Oxygen Index | 28.5 % | 28.5 % | ASTM D2863 |
| Shrinkage | 0.25 % | 0.25 % | 72 hr, 120oC; ASTM D1299 |