- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.075
- 缺口沖擊強度: 0.39
- 彎曲強度 [MPa]: 69.0
- 彎曲模量 [MPa]: 13.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.730 g/cc | 0.0264 lb/in3 | ASTM D1895 |
| Density | 1.75 g/cc | 0.0632 lb/in3 | ASTM D792 |
| Water Absorption | 0.075 % | 0.075 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00146 cm/cm | 0.00146 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 97 | 97 | ASTM D785 |
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 0.57 % | 0.57 % | ASTM D638 |
| Tensile Modulus | 14.3 GPa | 2070 ksi | ASTM D638 |
| Flexural Strength | 116 MPa | 16800 psi | ASTM D790 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | ASTM D790 |
| Compressive Strength | 252 MPa | 36500 psi | ASTM D695 |
| Poissons Ratio | 0.31 | 0.31 | ASTM D638 |
| Shear Modulus | 5.46 GPa | 792 ksi | Calculated |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ASTM D256 |
| Impact | 272 | 272 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.10e+12 ohm-cm | 3.10e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.2 | 5.2 | ASTM D150 |
| Dielectric Strength | 14.7 kV/mm | 373 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.0255 | 0.0255 | ASTM D150 |
| Arc Resistance | 115 sec | 115 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 226 °C | 439 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Shrinkage | 0.050 % | 0.050 % | 72 hr, 120oC; ASTM D1299 |