- 密度 [g/cm3]: 1.82
- 吸水率 [%]: 0.044
- 缺口沖擊強度: 0.161
- 彎曲強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.890 g/cc | 0.0322 lb/in3 | ASTM D1895 |
| Density | 1.82 g/cc | 0.0658 lb/in3 | ASTM D792 |
| Water Absorption | 0.044 % | 0.044 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 58 | 58 | ASTM D785 |
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Break | 0.52 % | 0.52 % | ASTM D638 |
| Tensile Modulus | 13.2 GPa | 1910 ksi | ASTM D638 |
| Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 128 MPa | 18600 psi | ASTM D695 |
| Izod Impact, Notched | 0.161 J/cm | 0.302 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.163 J/cm2 | 0.776 ft-lb/in2 | ASTM D256 |
| Impact | 59 | 59 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Shrinkage | 0.064 % | 0.064 % | 72 hr, 120oC; ASTM D1299 |