- 密度 [g/cm3]: 1.84
- 吸水率 [%]: 0.044
- 缺口沖擊強度: 0.162
- 彎曲強度 [MPa]: 42.0
- 彎曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.910 g/cc | 0.0329 lb/in3 | ASTM D1895 |
| Density | 1.84 g/cc | 0.0665 lb/in3 | ASTM D792 |
| Water Absorption | 0.044 % | 0.044 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0034 cm/cm | 0.0034 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 61 | 61 | ASTM D785 |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | 0.45 % | 0.45 % | ASTM D638 |
| Tensile Modulus | 13.9 GPa | 2020 ksi | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Compressive Strength | 117 MPa | 17000 psi | ASTM D695 |
| Izod Impact, Notched | 0.162 J/cm | 0.303 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.167 J/cm2 | 0.795 ft-lb/in2 | ASTM D256 |
| Impact | 61 | 61 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 210 °C | 410 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Shrinkage | 0.057 % | 0.057 % | 72 hr, 120oC; ASTM D1299 |