- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.045
- 缺口沖擊強度: 0.157
- 彎曲強度 [MPa]: 31.0
- 彎曲模量 [MPa]: 13.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1895 |
| Density | 1.74 g/cc | 0.0629 lb/in3 | ASTM D792 |
| Water Absorption | 0.045 % | 0.045 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00235 cm/cm | 0.00235 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 109 | 109 | ASTM D785 |
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 0.236 % | 0.236 % | ASTM D638 |
| Tensile Modulus | 15.1 GPa | 2190 ksi | ASTM D638 |
| Flexural Strength | 63.0 MPa | 9140 psi | ASTM D790 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | ASTM D790 |
| Compressive Strength | 142 MPa | 20600 psi | ASTM D695 |
| Poissons Ratio | 0.284 | 0.284 | ASTM D638 |
| Shear Modulus | 5.88 GPa | 853 ksi | Calculated |
| Izod Impact, Notched | 0.157 J/cm | 0.294 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.145 J/cm2 | 0.690 ft-lb/in2 | ASTM D256 |
| Impact | 35 | 35 | J/m drop Ball Impact; PLENCO |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 32.0 μm/m-°C @Temperature 40.0 - 130 °C | 17.8 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 1.94 W/m-K @Temperature 100 °C | 13.5 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| Oxygen Index | 41 % | 41 % | ASTM D2863 |
| Shrinkage | 0.073 % | 0.073 % | 72 hr, 120oC; ASTM D1299 |