- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.111
- 缺口沖擊強度: 0.164
- 彎曲強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 9.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in3 | ASTM D1895 |
| Density | 1.55 g/cc | 0.0560 lb/in3 | ASTM D792 |
| Water Absorption | 0.111 % | 0.111 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 79 | 79 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D638 |
| Tensile Modulus | 11.3 GPa | 1640 ksi | ASTM D638 |
| Flexural Strength | 89.0 MPa | 12900 psi | ASTM D790 |
| Flexural Modulus | 9.80 GPa | 1420 ksi | ASTM D790 |
| Compressive Strength | 180 MPa | 26100 psi | ASTM D695 |
| Izod Impact, Notched | 0.164 J/cm | 0.307 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.173 J/cm2 | 0.823 ft-lb/in2 | ASTM D256 |
| Impact | 93 | 93 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.20e+12 ohm-cm | 2.20e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 4.7 | 4.7 | ASTM D150 |
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Step by Step; ASTM D149 |
| 13.4 kV/mm | 340 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.046 | 0.046 | ASTM D150 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 48.0 μm/m-°C @Temperature 40.0 - 130 °C | 26.7 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.530 W/m-K @Temperature 100 °C | 3.68 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 206 °C | 403 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.510 mm | V-0 @Thickness 0.0201 in | |
| Oxygen Index | 39 % | 39 % | ASTM D2863 |
| Shrinkage | 0.14 % | 0.14 % | 72 hr, 120oC; ASTM D1299 |