- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.217
- 缺口沖擊強度: 0.166
- 彎曲強度 [MPa]: 53.0
- 彎曲模量 [MPa]: 8.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in3 | ASTM D1895 |
| Density | 1.54 g/cc | 0.0556 lb/in3 | ASTM D792 |
| Water Absorption | 0.217 % | 0.217 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0076 cm/cm | 0.0076 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 77 | 77 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.67 % | 0.67 % | ASTM D638 |
| Tensile Modulus | 9.90 GPa | 1440 ksi | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 8.60 GPa | 1250 ksi | ASTM D790 |
| Compressive Strength | 162 MPa | 23500 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 3.72 GPa | 540 ksi | Calculated |
| Izod Impact, Notched | 0.166 J/cm | 0.311 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.178 J/cm2 | 0.847 ft-lb/in2 | ASTM D256 |
| Impact | 98 | 98 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.50e+11 ohm-cm | 7.50e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.5 | 5.5 | ASTM D150 |
| Dielectric Strength | 6.60 kV/mm | 168 kV/in | Step by Step; ASTM D149 |
| 10.9 kV/mm | 277 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.057 | 0.057 | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.0 μm/m-°C @Temperature 40.0 - 130 °C | 25.6 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.540 W/m-K @Temperature 100 °C | 3.75 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |
| Shrinkage | 0.243 % | 0.243 % | 72 hr, 120oC; ASTM D1299 |