- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 0.21
- 斷裂伸長率 [%]: 84.1
- 彎曲強度 [MPa]: 54.3
- 彎曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | Apparent density per ASTM D1895 |
| Water Absorption | 0.35 % | 0.35 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0062 cm/cm | 0.0062 in/in | per ATM D955. Post shrinkage is 0.23% at 72hr 120oC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 91 | 91 | ASTM D785 |
| Tensile Strength, Ultimate | 54.3 MPa | 7880 psi | ASTM D638 |
| Elongation at Break | 0.72 % | 0.72 % | ASTM D638 |
| Tensile Modulus | 8.64 GPa | 1250 ksi | ASTM D638 |
| Flexural Yield Strength | 84.1 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Compressive Yield Strength | 218.9 MPa | 31750 psi | ASTM D695 |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.200 J/cm2 | 0.952 ft-lb/in2 | ASTM D256 |
| Impact | 120 | 120 | J/m Plenco drop ball test |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.42e+11 ohm-cm | 3.42e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz | 5.0 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 12.2 kV/mm | 310 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.051 @Frequency 1e+6 Hz | 0.051 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 195 °C | 383 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.10 mm | V-0 @Thickness 0.240 in | |