- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.224
- 缺口沖擊強(qiáng)度: 0.168
- 彎曲強(qiáng)度 [MPa]: 51.0
- 彎曲模量 [MPa]: 8.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in3 | ASTM D1895 |
| Density | 1.55 g/cc | 0.0560 lb/in3 | ASTM D792 |
| Water Absorption | 0.224 % | 0.224 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0082 cm/cm | 0.0082 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 77 | 77 | ASTM D785 |
| Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 0.54 % | 0.54 % | ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 |
| Flexural Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
| Compressive Strength | 159 MPa | 23100 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 4.07 GPa | 590 ksi | Calculated |
| Izod Impact, Notched | 0.168 J/cm | 0.315 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.169 J/cm2 | 0.804 ft-lb/in2 | ASTM D256 |
| Impact | 87 | 87 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 9.10e+11 ohm-cm | 9.10e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.2 | 5.2 | ASTM D150 |
| Dielectric Strength | 7.60 kV/mm | 193 kV/in | Step by Step; ASTM D149 |
| 11.0 kV/mm | 279 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.066 | 0.066 | ASTM D150 |
| Arc Resistance | 182 sec | 182 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 47.0 μm/m-°C @Temperature 40.0 - 130 °C | 26.1 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.540 W/m-K @Temperature 100 °C | 3.75 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 204 °C | 399 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 28.8 % | 28.8 % | ASTM D2863 |
| Shrinkage | 0.246 % | 0.246 % | 72 hr, 120oC; ASTM D1299 |
- 關(guān)鍵詞:
- 供應(yīng)
- Granular
- Injection Molded
- 酚醛樹脂
- Plenco 3356 Phenolic