- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.32
- 缺口沖擊強度: 0.184
- 彎曲強度 [MPa]: 54.0
- 彎曲模量 [MPa]: 8.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.630 g/cc | 0.0228 lb/in3 | ASTM D1895 |
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| Water Absorption | 0.32 % | 0.32 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 86 | 86 | ASTM D785 |
| Tensile Strength, Ultimate | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 0.74 % | 0.74 % | ASTM D638 |
| Tensile Modulus | 8.20 GPa | 1190 ksi | ASTM D638 |
| Flexural Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790 |
| Compressive Strength | 207 MPa | 30000 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.04 GPa | 441 ksi | Calculated |
| Izod Impact, Notched | 0.184 J/cm | 0.345 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.199 J/cm2 | 0.947 ft-lb/in2 | ASTM D256 |
| Impact | 100 | 100 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.60e+11 ohm-cm | 1.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.4 | 5.4 | ASTM D150 |
| Dielectric Strength | 11.6 kV/mm | 295 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.055 | 0.055 | ASTM D150 |
| Arc Resistance | 144 sec | 144 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 69.0 μm/m-°C @Temperature 40.0 - 130 °C | 38.3 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Maximum Service Temperature, Air | 203 °C | 397 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 26.1 % | 26.1 % | ASTM D2863 |
| Shrinkage | 0.267 % | 0.267 % | 72 hr, 120oC; ASTM D1299 |