- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.291
- 缺口沖擊強度: 0.184
- 彎曲強度 [MPa]: 59.0
- 彎曲模量 [MPa]: 8.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in3 | ASTM D1895 |
| Density | 1.42 g/cc | 0.0513 lb/in3 | ASTM D792 |
| Water Absorption | 0.291 % | 0.291 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0057 cm/cm | 0.0057 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 87 | 87 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 0.82 % | 0.82 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 94.0 MPa | 13600 psi | ASTM D790 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | ASTM D790 |
| Compressive Strength | 206 MPa | 29900 psi | ASTM D695 |
| Izod Impact, Notched | 0.184 J/cm | 0.345 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.198 J/cm2 | 0.942 ft-lb/in2 | ASTM D256 |
| Impact | 98 | 98 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.1 | 5.1 | ASTM D150 |
| Dielectric Strength | 11.4 kV/mm | 290 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.053 | 0.053 | ASTM D150 |
| Arc Resistance | 132 sec | 132 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 μm/m-°C @Temperature 40.0 - 130 °C | 38.9 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.400 W/m-K @Temperature 100 °C | 2.78 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 206 °C | 403 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 27.2 % | 27.2 % | ASTM D2863 |
| Shrinkage | 0.21 % | 0.21 % | 72 hr, 120oC; ASTM D1299 |