- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.202
- 缺口沖擊強度: 0.17
- 彎曲強度 [MPa]: 53.0
- 彎曲模量 [MPa]: 8.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.670 g/cc | 0.0242 lb/in3 | ASTM D1895 |
| Density | 1.57 g/cc | 0.0567 lb/in3 | ASTM D792 |
| Water Absorption | 0.202 % | 0.202 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0064 cm/cm | 0.0064 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 81 | 81 | ASTM D785 |
| Tensile Strength, Ultimate | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 0.97 % | 0.97 % | ASTM D638 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ASTM D638 |
| Flexural Strength | 84.0 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ASTM D790 |
| Compressive Strength | 181 MPa | 26300 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 3.20 GPa | 464 ksi | Calculated |
| Izod Impact, Notched | 0.170 J/cm | 0.318 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.195 J/cm2 | 0.928 ft-lb/in2 | ASTM D256 |
| Impact | 118 | 118 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.60e+11 ohm-cm | 3.60e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.2 | 5.2 | ASTM D150 |
| Dielectric Strength | 8.50 kV/mm | 216 kV/in | Step by Step; ASTM D149 |
| 12.8 kV/mm | 325 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.052 | 0.052 | ASTM D150 |
| Arc Resistance | 168 sec | 168 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 49.0 μm/m-°C @Temperature 40.0 - 130 °C | 27.2 μin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.450 W/m-K @Temperature 100 °C | 3.12 BTU-in/hr-ft2-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 197 °C | 387 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |
| Oxygen Index | 36 % | 36 % | ASTM D2863 |
| Shrinkage | 0.238 % | 0.238 % | 72 hr, 120oC; ASTM D1299 |