- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.54
- 缺口沖擊強度: 0.188
- 彎曲強度 [MPa]: 58.0
- 彎曲模量 [MPa]: 7.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.630 g/cc | 0.0228 lb/in3 | ASTM D1895 |
| Density | 1.39 g/cc | 0.0502 lb/in3 | ASTM D792 |
| Water Absorption | 0.54 % | 0.54 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0064 cm/cm | 0.0064 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 76 | 76 | ASTM D785 |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D638 |
| Elongation at Break | 0.88 % | 0.88 % | ASTM D638 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | ASTM D790 |
| Compressive Strength | 198 MPa | 28700 psi | ASTM D695 |
| Poissons Ratio | 0.36 | 0.36 | ASTM D638 |
| Shear Modulus | 2.76 GPa | 400 ksi | Calculated |
| Izod Impact, Notched | 0.188 J/cm | 0.352 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.196 J/cm2 | 0.933 ft-lb/in2 | ASTM D256 |
| Impact | 92 | 92 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.00e+12 ohm-cm | 8.00e+12 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.8 | 5.8 | ASTM D150 |
| Dielectric Strength | 7.50 kV/mm | 191 kV/in | Step by Step; ASTM D149 |
| 10.3 kV/mm | 262 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.053 | 0.053 | ASTM D150 |
| Arc Resistance | 131 sec | 131 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 182 °C | 360 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.43 % | 0.43 % | 72 hr, 120oC; ASTM D1299 |