- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 17.0
- 斷裂伸長率 [%]: 482
- 彎曲強度 [MPa]: 324.0
- 彎曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 68 | 68 | ASTM D2583 |
| Tensile Strength, Ultimate | 324 MPa | 47000 psi | ASTM D638 |
| Flexural Yield Strength | 482 MPa | 69900 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2490 ksi | ASTM D790 |
| Izod Impact, Notched | 17.0 J/cm | 31.8 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL Recognized |
| >= 260 °C | >= 500 °F | Deflection Temp; Load not reported; ASTM D648 | |
| Flammability, UL94 | V-1 @Thickness 2.90 mm | V-1 @Thickness 0.114 in | |
| Shrinkage | 0.0010 % | 0.0010 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 149 °C | 270 - 300 °F | Mold temperature |