- 密度 [g/cm3]: 1.85
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 14.4
- 斷裂伸長率 [%]: 310
- 彎曲強度 [MPa]: 193.0
- 彎曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in3 | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 58 | 58 | ASTM D2583 |
| Tensile Strength, Ultimate | 193 MPa | 28000 psi | ASTM D638 |
| Tensile Modulus | 17.9 GPa | 2600 ksi | ASTM D638 |
| Flexural Yield Strength | 310 MPa | 45000 psi | ASTM D790 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ASTM D790 |
| Compressive Yield Strength | 172 MPa | 24900 psi | ASTM D695 |
| Izod Impact, Notched | 14.4 J/cm | 27.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Shrinkage | 0.0010 % | 0.0010 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 157 °C | 270 - 315 °F | Mold temperature |