| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.95 g/cc | 1.95 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00 cm/cm | 0.00 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 68 | 68 | ASTM D2583 |
| Tensile Strength | 483 MPa | 70100 psi | ASTM D638 |
| Flexural Strength | 931 MPa | 135000 psi | ASTM D790 |
| Flexural Modulus | 34.5 GPa | 5000 ksi | ASTM D790 |
| Izod Impact, Notched | 22.24 J/cm | 41.66 ft-lb/in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 149 °C @Thickness 12.7 mm | 270 - 300 °F @Thickness 0.500 in | Compression Molding |
| Clamp Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C | 0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F | |
| Shelf Life | 2.00 Month @Temperature 23.9 °C | 2.00 Month @Temperature 75.0 °F | |