- 吸水率 [%]: 0.13
- 缺口沖擊強度: 9.6
- 彎曲模量 [MPa]: 11.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Water Absorption | 0.13 % | 0.13 % | ASTM D570 | ||
| 1.2 % @Temperature 50.0 °C, Time 3.60e+6 sec | 1.2 % @Temperature 122 °F, Time 1000 hour | ASTM D570 | |||
| Linear Mold Shrinkage | -0.00100 cm/cm | -0.00100 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 105 MPa | 15200 psi | ASTM D638 | ||
| Flexural Strength | 235 MPa | 34100 psi | ASTM D790 | ||
| Flexural Modulus | 11.4 GPa | 1650 ksi | ASTM D790 | ||
| Izod Impact, Notched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | >= 250 °C | >= 482 °F | Deflection Temperature, Load not specified; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 132 - 160 °C @Thickness 12.7 mm | 270 - 320 °F @Thickness 0.500 in | Compression Molding | ||
| Clamp Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |||
| Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 149 °C | 0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 300 °F | |||
| Shelf Life | 1.00 Month @Temperature 23.9 °C | 1.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Fiber Length (in) | 1 | Glass, nominal | |||
| Flammability | Self Extinguishing | FMVSS 302-75 | |||