- 吸水率 [%]: 0.15
- 缺口沖擊強度: 16.0
- 彎曲模量 [MPa]: 15.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 | ||
| Linear Mold Shrinkage | 0.00050 cm/cm | 0.00050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 58 | 58 | ASTM D2583 | ||
| Tensile Strength | 220 MPa | 31900 psi | ASTM D638 | ||
| Flexural Strength | 400 MPa | 58000 psi | ASTM D790 | ||
| Flexural Modulus | 15.8 GPa | 2290 ksi | ASTM D790 | ||
| Compressive Strength | 172 MPa | 24900 psi | ASTM D695 | ||
| Shear Modulus | 4.50 GPa | 653 ksi | ASTM D4065 | ||
| Izod Impact, Notched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | >= 260 °C | >= 500 °F | Deflection Temperature, Load not specified; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 132 - 157 °C | 270 - 315 °F | Compression Molding | ||
| Clamp Pressure | 2.76 - 8.27 MPa | 400 - 1200 psi | |||
| Cure Time | 1.25 min @Thickness 1.52 mm, Temperature 143 °C | 0.0208 hour @Thickness 0.0600 in, Temperature 290 °F | |||
| Shelf Life | 1.00 Month @Temperature 23.9 °C | 1.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Fiber Length (in) | 1 | Glass, nominal | |||
| Flammability | Self Extinguishing | ISO 3795 | |||